表1 粉煤灰的物理性質
粉煤灰中SiO2、Al2O3、Fe2O3 3種成分占70%以上，CaO和MgO量較小，CaO和MgO的含量隨原煤的組成和產出時代不同而變化，一般在0.2%～10%之間變動。粉煤灰主要由非晶態玻璃相構成，其中石英為主要結晶相。粉煤灰中礦物狀態的構成比率受炭質和燃燒冷卻條件控制，其pH值可從弱堿性向強堿性過渡[3]。
粉煤灰的綜合利用
目前，粉煤灰綜合利用的渠道主要集中在建筑工程、道路工程及農業用灰等方面，“八五”期間的統計分析見表2[4]。
途徑
用灰總量（×104t）
所占比例
建材用灰
4982
32.2
筑路用灰
3960
25.7
回填用灰
3206
20.8
建工用灰
1481
9.6
農業用灰
843
5.5
上一頁 [1] [2] [3] [4] [5] [6] [7] [8] [9] [10] [11] [12] [13] [14] [15] [16] [17] [18] [19] [20] [21] [22] [23] [24] [25] [26] [27] [28] [29] [30] [31] [32] [33] [34] [35] [36] [37] [38] [39] [40] [41] [42] [43] [44] [45] [46] [47] [48] [49] [50] [51] [52] [53] [54] [55] [56] [57] [58] [59] [60] [61] [62] [63] [64] [65] [66] [67] [68] [69] [70] [71] [72] [73] [74] [75] [76] [77] [78] [79] [80] [81] [82] [83] [84] [85] [86] [87] [88] [89] [90] [91] [92] [93] [94] [95] [96] [97] [98] [99] [100] [101] [102] [103] [104] [105] [106] [107] [108] [109] [110] 下一頁